Covestro Bayblend® FR 86 Polycarbonate/ABS Blend

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Covestro
Trade Name	Bayblend®
Port	Shanghai port, China
Download PDF	Covestro Bayblend® FR 86 Polycarbonate/ABS Blend.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Easy-flowing FR grade. Flame retardant grade with antimony, chlorine and bromine free, flame retardant package.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.

Mechanical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³
Water Absorption	0.70 %	0.70 %	Saturation in water
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Equilibrium at 50% RH
Water Absorption at Saturation	0.70 %	0.70 %
Melt Flow	50 g/10 min <br>@Load 5.00 kg,<br> Temperature 240 °C	50 g/10 min <br>@Load 11.0 lb,<br> Temperature 464 °F

Thermal Properties	Metric	English
Tensile Strength, Yield	58.0 MPa	8410 psi
Elongation at Yield	3.5 %	3.5 %
Tensile Modulus	2.60 GPa	377 ksi

Optical Properties	Metric	English
CTE, linear, Parallel to Flow	76.0 µm/m-°C <br>@Temperature 20.0 °C	42.2 µin/in-°F <br>@Temperature 68.0 °F
CTE, linear, Transverse to Flow	80.0 µm/m-°C <br>@Temperature 20.0 °C	44.4 µin/in-°F <br>@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	82.0 °C	180 °F
Deflection Temperature at 1.8 MPa (264 psi)	72.0 °C	162 °F
Vicat Softening Point	84.0 °C	183 °F
UL RTI, Electrical	60.0 °C <br>@Thickness 1.50 mm	140 °F <br>@Thickness 0.0591 in
UL RTI, Mechanical with Impact	60.0 °C <br>@Thickness 1.50 mm	140 °F <br>@Thickness 0.0591 in
UL RTI, Mechanical without Impact	60.0 °C <br>@Thickness 1.50 mm	140 °F <br>@Thickness 0.0591 in
Flammability, UL94	V-0 <br>@Thickness 1.60 mm	V-0 <br>@Thickness 0.0630 in
Oxygen Index	30 %	30 %

Chemical Resistance Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm
Dielectric Constant	2.9 <br>@Frequency 1e+6 Hz	2.9 <br>@Frequency 1e+6 Hz
	3.0 <br>@Frequency 100 Hz	3.0 <br>@Frequency 100 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.0050 <br>@Frequency 100 Hz	0.0050 <br>@Frequency 100 Hz
	0.0070 <br>@Frequency 1e+6 Hz	0.0070 <br>@Frequency 1e+6 Hz
Comparative Tracking Index	300 V	300 V