Covestro Bayblend® FR 2000 Polycarbonate/ABS Blend  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® FR 2000 Polycarbonate/ABS Blend  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Easy-flowing FR grade. Flame retardant grade with antimony, chlorine and bromine free, flame retardant package, optimized processability.Applications: Housings for office equipment, electrical engineering, computer sectors.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Water Absorption 0.70 %
0.70 %
Saturation in water
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Equilibrium at 50% RH
Water Absorption at Saturation 0.70 %
0.70 %
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 30 g/10 min

@Load 5.00 kg,
Temperature 240 °C
30 g/10 min

@Load 11.0 lb,
Temperature 464 °F
Spiral Flow 76.0 cm

@Thickness 2.50 mm
29.9 in

@Thickness 0.0984 in
at 254°C melt temp.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
Elongation at Break 70 %
70 %
ASTM D638
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 2.70 GPa
392 ksi
Flexural Yield Strength 95.0 MPa
13800 psi
at 5% strain; ASTM D790
Flexural Modulus 2.70 GPa
392 ksi
ASTM D790
Izod Impact, Notched 4.30 J/cm

@Thickness 3.20 mm
8.06 ft-lb/in

@Thickness 0.126 in
ASTM D256
Impact Test 49.0 J

@Thickness 3.20 mm
36.1 ft-lb

@Thickness 0.126 in
Instrumented Total Impact; 3.2 mm thick, 12.5 mm dart, 75 mm clamp, 6.7 m/s; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 76.0 µm/m-°C

@Temperature 20.0 °C
42.2 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 20.0 °C
44.4 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
Vicat Softening Point 92.0 °C
198 °F
UL RTI, Electrical 90.0 °C
194 °F
UL RTI, Mechanical with Impact 75.0 °C
167 °F
UL RTI, Mechanical without Impact 85.0 °C
185 °F
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Oxygen Index 34 %
34 %
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
3.0

@Frequency 100 Hz
3.0

@Frequency 100 Hz
Dielectric Strength 30.0 kV/mm
762 kV/in
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
0.0070

@Frequency 1e+6 Hz
0.0070

@Frequency 1e+6 Hz
Comparative Tracking Index 300 V
300 V
Processing Properties Metric English Comments
Melt Temperature 220 - 270 °C
428 - 518 °F