Cossa Polimeri ESTADIENE 1218 V0 Flame Retardant ABS

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer	Cossa Polimeri S.r.L.
Trade Name	ESTADIENE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cossa Polimeri ESTADIENE 1218 V0 Flame Retardant ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Acrylonitrile Butadiene StyreneFlame retardant class V0, PBDE free, good impact resistance, excellent processability, good surface appearance, good thermal resistanceInformation provided by Cossa Polimeri S.r.l.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	ASTM D 792
Linear Mold Shrinkage	0.0030 - 0.0060 cm/cm	0.0030 - 0.0060 in/in	ASTM D 955
Melt Flow	25 g/10 min @Load 10.0 kg, Temperature 220 °C	25 g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	30.0 MPa	4350 psi	ASTM D 638
Tensile Strength, Yield	40.0 MPa	5800 psi	ASTM D 638
Elongation at Break	5.0 %	5.0 %	ASTM D 638
Flexural Modulus	2.50 GPa	363 ksi	ASTM D 790
Izod Impact, Notched	0.900 J/cm @Temperature 0.000 °C	1.69 ft-lb/in @Temperature 32.0 °F	ASTM D 638
	1.10 J/cm @Temperature 23.0 °C	2.06 ft-lb/in @Temperature 73.4 °F	ASTM D 256

Thermal Properties	Metric	English	Comments
Vicat Softening Point	94.0 °C @Load 5.00 kg	201 °F @Load 11.0 lb	50°C/hr; ASTM D 1525
	104 °C @Load 0.999 kg	219 °F @Load 2.20 lb	50°C/hr; ASTM D 1525
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Glow Wire Test	960 °C	1760 °F	I.E.C. 695-2-1

Users viewing this material also viewed the following: