Cosmic Plastics E484 Glass Filled Epoxy Molding Compound, Electrical Grade
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics E484 Glass Filled Epoxy Molding Compound, Electrical Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.95 g/cc | 0.0704 lb/in³ | |
| Apparent Bulk Density | 0.780 g/cc | 0.0282 lb/in³ | |
| Water Absorption | 0.20 % | 0.20 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Barcol | 70 | 70 | |
| Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | |
| Flexural Strength | 131 MPa | 19000 psi | |
| Flexural Modulus | 18.0 GPa | 2610 ksi | |
| Compressive Strength | 207 MPa | 30000 psi | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.4187 W/m-K | 2.906 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 230 °C | >= 446 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | |
| Dielectric Constant | 4.7 @Frequency 1e+6 Hz |
4.7 @Frequency 1e+6 Hz |
Wet |
| 5.4 @Frequency 1000 Hz |
5.4 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
Wet |
| 0.011 @Frequency 1000 Hz |
0.011 @Frequency 1000 Hz |
Wet | |
| Arc Resistance | 186 sec | 186 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 150 - 175 °C | 302 - 347 °F | Molding temperature |
Users viewing this material also viewed the following:
- Osprey Metals Co502 Cobalt Alloy Powder (Grade 80% - 22)
- Total 965E Polystyrene (discontinued **)
- SABIC Innovative Plastics Lexan® FXE173R PC
- LG Chemical LUPOY NS5000 PC/ABS, High Impact
- Spartech 3130-85 PVC and Alloy Products for Wire and Cable
- A. Schulman POLYFORT™ FPP 3717 Talc Filled Homopolymer Polypropylene (39.6% Mineral Content)
- Clariant PBTSP0008WT-199 Polybutylene Terephthalate, Glass Reinforced, Flame Retardant
- China-Yixing Longly Refractories ASM-120 Cordierite-Mullite
Copyright © lookpolymers.com All Rights Reserved