C.O.I.M. LARIPUR® LPR5850 Modified Ester Polyurethane

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer , Polyurethane, TP
Manufacturer	C.O.I.M. S.p.A.
Trade Name	Laripur®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	C.O.I.M. LARIPUR® LPR5850 Modified Ester Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: The products of the LARIPUR® line are thermoplastic polyurethanes. These products combine the technology of thermoplastic products with the features of polyurethanes:Excellent abrasion resistanceGreat flexibility with constancy at temperature variationsGood compression resistanceGood water and light resistanceGood resistance to oils, fats and to many types of solventsSeries 50 Modified Ester: These products are obtained by homogeneously incorporating a small amount of raw material of unique chemical composition to the products of Series 25. They combine a high level of hardness with excellent cold impact resistance.Information provided by P.A.T. Products, Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.18 g/cc	1.18 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	58	58	ASTM D2240
Tensile Strength, Yield	63.5 MPa	9210 psi	ASTM D412
Elongation at Break	430 %	430 %	ASTM D412
50% Modulus	0.0156 GPa	2.26 ksi	ASTM D412
100% Modulus	0.0180 GPa	2.61 ksi	ASTM D412
300% Modulus	0.0430 GPa	6.24 ksi	ASTM D412
Flexural Modulus	0.270 GPa	39.2 ksi	ASTM D790
Izod Impact, Notched (ISO)	12.6 kJ/m² @Temperature -20.0 °C	6.00 ft-lb/in² @Temperature -4.00 °F	ASTM D256
Tear Strength	165 kN/m	941 pli	ASTM D624
Abrasion	40	40	mm3, Abrasion Loss; DIN 53516
Torsional Stiffness	67.0 MPa	9720 psi	+20°C; ASTM D1043
	306 MPa	44400 psi	-20°C; ASTM D1043

Thermal Properties	Metric	English	Comments
Vicat Softening Point	120 °C	248 °F	ASTM D1525