- Chi Mei Wonderloy® PC-510 PC/ABS Alloy - Flame Retardant
Chi Mei Wonderloy® PC-510 PC/ABS Alloy - Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Wonderloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Wonderloy® PC-510 PC/ABS Alloy - Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Flow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 |
| Melt Flow | 23.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
23.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 55 % | 55 % | 50 mm/min; ISO 527 |
| Flexural Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | ISO 180/4A |
| Charpy Impact, Notched | 3.10 J/cm² | 14.8 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | annealed; ISO 75 |
| 87.0 °C | 189 °F | unannealed; ISO 75 | |
| Vicat Softening Point | 88.0 °C @Load 5.00 kg |
190 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 95.0 °C @Load 1.00 kg |
203 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0590 in |
Users viewing this material also viewed the following:
- Omnia Plastica PE 500 - Polyethylene 500
- Polymer Resources PPX-GP4 Modified PPO, General Purpose with HDT of 210 F (Unverified Data**)
- 3M Dyneon™ CC603 PTFE, 15% Fiberglass Filled (discontinued **)
- Lord Adhesives Aeroglaze® 9929 Epoxy Primer
- Lehmann & Voss LUVOCOM® 1106-8133 Polyether imide, with carbon fiber, easy flowing
- Teknor Apex Monprene® MP-1500L2 Thermoplastic Elastomer
- Master Bond EP17HT-3 One component, snap-curing epoxy system
- 3M 12030 Black 1/2" (12.7 mm) Polyurethane Foam
- Unifrax Fiberfrax® 970 Ceramic Fiber Paper
Copyright © lookpolymers.com All Rights Reserved