Network Polymers Softflex® 5000
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 5000.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.877 g/cc | 0.877 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0229 cm/cm @Thickness 3.17 mm |
0.0229 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0153 cm/cm @Thickness 3.17 mm |
0.0153 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 1.1 g/10 min @Load 1.00 kg, Temperature 235 °C |
1.1 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| 3.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A Condition L; ASTM D1238 | |
| 5.4 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.4 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 - 50 | 40 - 50 | 10 second dwell; ASTM D2240 |
| 45 - 55 | 45 - 55 | Instantaneous; ASTM D2240 | |
| Tensile Strength at Break | 8.83 MPa | 1280 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | >= 1000 % | >= 1000 % | ASTM D412 |
| 50% Modulus | 0.000740 GPa | 0.107 ksi | ASTM D412 |
| 100% Modulus | 0.000950 GPa | 0.138 ksi | ASTM D412 |
| 300% Modulus | 0.00163 GPa | 0.236 ksi | ASTM D412 |
| Flexural Modulus | 0.00536 GPa | 0.777 ksi | Test Method I (chs speed 0.5 in/min); ASTM D790 |
| Tear Strength | 21.1 kN/m | 120 pli | Die C/20"/min; ASTM D624 |
| Compression Set | 18.8 % | 18.8 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
| 89.4 % @Temperature 70.0 °C |
89.4 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| Tensile Set | 6.8 % | 6.8 % |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® PE 1296 Conductive Thermoplastic Compound
- Pinnacle Polymers 1704 Polypropylene Homopolymer, Stretched Tape Grade
- Shakespeare Isocorâ„¢ HZ73SI high viscosity PA-6
- SABIC Innovative Plastics Ultem ATX203R PEI+PCE
- A. Schulman FORMION™ FI 226 40% Glass Fiber Reinforced Ionomer / Nylon Alloy
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 20.0 PHR Wacker HDK N20 Filler
- 3D Systems Accura® ClearVue™ Free (SL 7870) Stereolithography Plastic
- ArcelorMittal 06 High formability steel for drawing, Cold rolled
- Wellman Wellamid® XT1863-BK1 Impact Modified Nylon 66
Copyright © lookpolymers.com All Rights Reserved