Chi Mei Wonderlite® PC-110L Polycarbonate - UV Stabilized

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, UV Stabilized
Manufacturer Chi Mei Corporation (ChiMei)
Trade Name Wonderlite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chi Mei Wonderlite® PC-110L Polycarbonate - UV Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Head Lamp
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 Melt Volume Rate (ml/10 min); ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 100 MPa
14500 psi
H358/30; ISO 2039-1
Tensile Strength at Break 75.0 MPa
10900 psi
50 mm/min; ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527
Elongation at Break 120 %
120 %
50 mm/min; ISO 527
Flexural Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 80.0 kJ/m²
38.1 ft-lb/in²
ISO 180/4A
Charpy Impact, Notched 7.50 J/cm²
35.7 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
annealed; ISO 75
142 °C
288 °F
unannealed; ISO 75
Vicat Softening Point 143 °C

@Load 5.00 kg
 289 °F

@Load 11.0 lb
 50°C/hr; ISO 306
148 °C

@Load 1.00 kg
 298 °F

@Load 2.20 lb
 50°C/hr; ISO 306
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0590 in