Multibase Multi-Flex® TPE A 8502 BLK
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® TPE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TPE A 8502 BLK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The fogging test value is 90% according to ASTM SAE-J275. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 - 1.03 g/cc | 0.0350 - 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 3.5 - 8.5 g/10 min | 3.5 - 8.5 g/10 min | (Condition L) ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | 10 sec; ASTM D-2240 |
| Tensile Strength, Ultimate | 9.00 - 13.0 MPa | 1310 - 1890 psi | ASTM D412 |
| Elongation at Break | 600 - 800 % | 600 - 800 % | ASTM D412 |
| Flexural Modulus | 0.0350 - 0.0550 GPa | 5.08 - 7.98 ksi | method 1, Proc.B; ASTM D-790 |
| Tear Strength | 39.0 - 49.0 kN/m | 223 - 280 pli | ASTM D624 |
| Compression Set | 25 % | 25 % | for 70 hours at 23°C; ASTM 395 |
| 55 % @Temperature 70.0 °C |
55 % @Temperature 158 °F |
for 70 hours at 70°C; ASTM 395 | |
| 76 % @Temperature 100 °C |
76 % @Temperature 212 °F |
70 hours at 100°C; ASTM 395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 140 °C | 284 °F |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ FR PE 161 HDPE (discontinued **)
- Solvay Specialty Polymers Ixef® 1622 Polyarylamide (PARA) (Unverified Data**)
- Gouda Vuurvast CURON 127 S GM Dense Refractory Castable
- SABIC Innovative Plastics LNP LUBRICOMP PFI12R PA 6
- Entec Hypro™ PPH-CC30 Natural Homopolymer Polypropylene, 30% Calcium Carbonate Filled
- Fainplast Compounds Hax™ HFX 505 Crosslinkable HFFR Cable Compound
- Braskem H 502 HC Injection Molding Polypropylene
- 3M Dyneon™ FE 5522 Fluoroelastomer
- Asahi Kasei Thermylene® P7-20FG-0610 20% Glass Fiber Reinforced, Heat Stabilized
- Alliance BIN-55 Bonded (Composite) Magnetic Material
Copyright © lookpolymers.com All Rights Reserved