Chi Mei Polyrex® PG-80N Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polyrex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polyrex® PG-80N Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High strength
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Melt Flow | 6.2 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.2 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 76.0 MPa | 11000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | unannealed; ISO 75 |
| Vicat Softening Point | 92.0 °C @Load 5.00 kg |
198 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 97.0 °C @Load 1.00 kg |
207 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 100 °C @Load 1.00 kg |
212 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Mallard Creek Polymers Rovene® 4119 Styrene-Butadiene Emulsion
- Silberline Extra Fine "O" Standard Series
- SMAC CABLE® 2516S-40-10 Damping Material
- Universal Wire Works 312 Stainless Steel Electrode
- Hexcel® Redux® 335U Adhesive film for bonding metallic and composite components (0.03 psf)
- Eagle Brass 220 Commercial Bronze, 1/4 Hard
- DuPont Performance Polymers Crastin® LW9030FR NC010 PBT+ASA (Unverified Data**)
- Arlon 51588R019 0.019" (0.483 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M FV090 Soft Translucent Vinyl Label Products
- Bhansali Engineering Abstron IMG-1115 Glass Reinforced Grade
Copyright © lookpolymers.com All Rights Reserved