Chi Mei Polylac® PA-747R ABS - Extrusion
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-747R ABS - Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Attach case and refrigerator
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.30 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.30 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 2.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
2.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; ISO 527 |
| Flexural Strength | 61.0 MPa | 8850 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 3.60 J/cm @Thickness 6.35 mm |
6.74 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.27 J/cm @Thickness 3.17 mm |
8.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 3.20 J/cm² | 15.2 ft-lb/in² | ISO 179 |
| Impact | 21.0 | 21.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | unannealed; ISO 75 |
| 99.0 °C | 210 °F | annealed; ISO 75 | |
| Vicat Softening Point | 101 °C @Load 5.00 kg |
214 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 104 °C @Load 5.00 kg |
219 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 106 °C @Load 1.00 kg |
223 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 108 °C @Load 1.00 kg |
226 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Plaskolite Vivak PETG Sheet
- Precision Polymer Engineering S70T Silicone Rubber
- Reltek BONDiT™ B-451 Adhesive and Sealant
- LTL Color Compounds ColorRxâ„¢ PE2-0202ARX Biocompatible, Antimicrobial HDPE
- Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/HS/BK Polyamide 66, with glass fiber and PTFE, heat stabilized
- Indium Corp. Indalloy® 165 Pb-Ag-Sn Solder Alloy
- Borealis Borclear™ RF366MO Polypropylene Random Copolymer for Injection Molding
- Unitika A3030N-2 PA6, 30% Mineral Reinforced, Conditioned
- 3M FM010 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- 3M Scotch® 896 Filament Tape
Copyright © lookpolymers.com All Rights Reserved