Chase Plastics CP Pryme® N130L Nylon 6, 30% Glass Fiber Reinforced, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® N130L Nylon 6, 30% Glass Fiber Reinforced, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: LubricatedForm: PelletsInformation provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 1.3 % | 1.3 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 176 MPa | 25500 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG94 ABS (Asia Pacific)
- Polykemi AB POLYfill PPH GF15030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- M. Holland Company CP910 Polypropylene Impact Copolymer
- Michelman® Michem® Emulsion 37135 Nonionic polyethylene emulsion
- Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes
- SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER (Europe-Africa-Middle East)
- Zircar Zirconia HfF-15 Hafnia Knit Textile Insulation
- Covestro Bayblend® T 45 MN Polycarbonate/ABS Blend
- Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 718°C (1325°F)/8hr/AC to 621°C (1150°F)/8hr/AC
- NOVA Chemicals Sclair® TD-7915-U Hexene MDPE Rotational Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved