Chang Chun Plastic PBT4815 Fire Retardant & 15% Glass Fiber Enforced Grade PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Chang Chun Plastic Co. Ltd. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chang Chun Plastic PBT4815 Fire Retardant & 15% Glass Fiber Enforced Grade PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Dowell Trading Company Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 - 1.52 g/cc | 0.0517 - 0.0549 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.020 cm/cm | 0.0040 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 93 | 93 | ASTM D785 |
| Tensile Strength, Ultimate | 90.0 - 110 MPa | 13100 - 16000 psi | ASTM D638 |
| Elongation at Break | 4.0 - 5.5 % | 4.0 - 5.5 % | ASTM D638 |
| Flexural Yield Strength | 140 - 180 MPa | 20300 - 26100 psi | ASTM D790 |
| Flexural Modulus | 4.50 - 6.50 GPa | 653 - 943 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 - 0.700 J/cm @Thickness 6.35 mm |
0.937 - 1.31 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C @Temperature 20.0 °C |
30.6 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 60 Hz |
3.3 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60 Hz |
0.0010 @Frequency 60 Hz |
ASTM D150 |
| Arc Resistance | 90 sec | 90 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Omnia Plastica PE 1000 - Polyethylene 1000
- Polymer Resources PPX-FR3 Modified-PPO, V-1 Flame Retardant
- Nylene® Naxel™ PC35CV Polycarbonate
- Gouda Vuurvast FLUCON 160 K Dense Self Flowing Refractory Castable
- Sibur O-40 Compound OM-40 Polyvinyl Chloride (PVC)
- Techmer ES Plaslube® J-3/30/TF/15 Nylon 6, 30% GFR, 15% PTFE
- Supreme Petrochem SC 208 General Purpose Polystyrene
- Hexcel® HexForce™ 2313 Fiber Glass Fabric
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 40% Cold Rolled (UNS S30400)
Copyright © lookpolymers.com All Rights Reserved