BASF Ultramid® 8270 HS BK 102 PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8270 HS BK 102 PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Ultramid 8270 HS BK-102 is a thermally modified pigmented black, PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requiring extra high melt viscosity. It exhibits excellent permeability and chemical resistance to oils, hydrocarbons and most solvents.Applications: Industrial containers, small gasoline tanks, and automotive under hood reservoirs.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ASTM D792
Moisture Absorption at Equilibrium	1.6 %	1.6 %	24 Hours; ASTM D570
	2.6 %	2.6 %	50% RH; ASTM D570
	9.2 %	9.2 %	Saturation; ASTM D570

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	46.0 MPa @Temperature 23.0 °C	6670 psi @Temperature 73.4 °F	ASTM D638
	119 MPa @Temperature -40.0 °C	17300 psi @Temperature -40.0 °F	ASTM D638
Flexural Strength	37.0 MPa @Temperature 23.0 °C	5370 psi @Temperature 73.4 °F	ASTM D790
	176 MPa @Temperature -40.0 °C	25500 psi @Temperature -40.0 °F	ASTM D790
Flexural Modulus	0.760 GPa @Temperature 23.0 °C	110 ksi @Temperature 73.4 °F	ASTM D790
	3.90 GPa @Temperature -40.0 °C	566 ksi @Temperature -40.0 °F	ASTM D790
Izod Impact, Notched	0.480 J/cm @Temperature -40.0 °C	0.899 ft-lb/in @Temperature -40.0 °F	ASTM D256
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ASTM D256

Processing Properties	Metric	English
Melt Temperature	245 - 260 °C	473 - 500 °F
Mold Temperature	60.0 °C	140 °F
Dry Time	2 - 4 hour	2 - 4 hour
Moisture Content	<= 0.15 %	<= 0.15 %

Descriptive Properties	Value	Comments
Color	BK 102
Commercial Status	North America