Network Polymers Softflex® 0826
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 0826.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.947 g/cc | 0.947 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Thickness 3.17 mm |
0.017 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm @Thickness 3.17 mm |
0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 2.1 g/10 min @Load 1.00 kg, Temperature 235 °C |
2.1 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 31 - 41 | 31 - 41 | 10 second dwell; ASTM D2240 |
| 35 - 45 | 35 - 45 | Instantaneous; ASTM D2240 | |
| Tensile Strength, Yield | 6.89 MPa | 1000 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | 846 % | 846 % | ASTM D412 |
| 50% Modulus | 0.000700 GPa | 0.102 ksi | ASTM D412 |
| 100% Modulus | 0.00100 GPa | 0.145 ksi | ASTM D412 |
| 300% Modulus | 0.00200 GPa | 0.290 ksi | ASTM D412 |
| Gardner Impact | 12.51 J @Temperature -30.0 °C |
9.225 ft-lb @Temperature -22.0 °F |
ASTM D5420 |
| Tear Strength | 21.0 kN/m | 120 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 0.2929 | 0.2929 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 14.4 % | 14.4 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
| 76.6 % @Temperature 70.0 °C |
76.6 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| Tensile Set | 15.5 % | 15.5 % | 100% strain; ASTM D412 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 7781 E-Glass Reinforced
- Polymer Resources TPSF-G10 Polybutylene Terephthalate, Structural Foam, 10% Glass Reinforced
- DuPont™ Sclairfilm® MPP-3 LLDPE Film, "Super Strength", 25 µm Thickness (discontinued **)
- Kazanorgsintez E-5 Petroleum Resin
- Sylvin Technologies 9600-90 Clear PVC Molding Compound
- Techmer ES HiFill® PA6/6 GF33 NAT001 33% Glass Filled
- SK Chemicals SKYTHANE® S185A Polyester Based Thermoplastic Polyurethane Elastomer
- Solvay IGEPAL® RC 520 Surfactant
- DSM Arnitel® PL381-H TPC-ET
- ExxonMobil Enable™ 20-10CE Metallocene Polyethylene Resin (Africa & Middle East Grade)
Copyright © lookpolymers.com All Rights Reserved