CP-Polymer-Technik Wellamid® 6600 MR 209 HWCP 20% Mineral Nylon 66, Heat Stabilized, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6600 MR 209 HWCP 20% Mineral Nylon 66, Heat Stabilized, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.0 - 2.5 % | 2.0 - 2.5 % | 23°C/50%RH, Starting when dry; DIN 53495 |
| Linear Mold Shrinkage | 0.0090 - 0.011 cm/cm @Thickness 4.00 mm |
0.0090 - 0.011 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 18 % | 18 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.90 GPa | 276 ksi | ISO 527 |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 °C | 491 °F | Kofler |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | ISO 3915 |
| Dielectric Constant | 6.0 @Frequency 1e+6 Hz |
6.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.060 | 0.060 | At 1 MHz; IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 265 - 295 °C | 509 - 563 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | High | |
| Screw Speed | Medium |
Users viewing this material also viewed the following:
- Reliance Industries Repol B550MN Polypropylene
- Quadrant EPP Quadrant PC 1000 Extruded, Unfilled, Polycarbonate (ASTM Product Data Sheet)
- Fiberfil® J-60/30/E8/M Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled
- Plenco 1501 Polyester, Briquette, Compression Molded
- A. Schulman POLYBATCH™ Blue LL40445/2 Concentrate Based In LLDPE
- Tipco Tipcolite® TPF 1011 - Unreinforced Thermoset Phenolic Resin, 43 mm Norton Flow without Hexamine
- Hexcel® HexPly® M36 180°C (350°F) Curing Epoxy Matrix, Unidirectional Prepreg Laminate (M36/32%/135/HTA)
- 3M FM113 Indoor UL Recognized Brushed Silver Polyester Label Products
- Fainplast Compounds PM 6510/K Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved