CENTROPLAST CENTROLYTE FG Polyethylene terephthalate, Food Grade
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced |
| Manufacturer | CENTROPLAST Engineering Plastics GMBH |
| Trade Name | CENTROLYTE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CENTROPLAST CENTROLYTE FG Polyethylene terephthalate, Food Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This material is electrically insulating, with good chemical resistance, high mechanical strength and wear resistance.Information provided by CENTROPLAST Engineering Plastics GMBH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | in normal climate 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | in water at 23°C; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 @Thickness 10.0 mm |
95 @Thickness 0.394 in |
ISO 2039-2 |
| Ball Indentation Hardness | 170 MPa | 24700 psi | value at 30 sec.; ISO 2039-1 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | v = 50 mm/min; ISO 527-2 |
| Elongation at Break | 15 % | 15 % | ISO 527-2 |
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527-2 |
| Charpy Impact Unnotched | >= 5.00 J/cm² | >= 23.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | |
| Melting Point | 255 °C | 491 °F | 10K/min; ISO 3146 |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Long Term |
| 160 °C | 320 °F | Short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| HB @Thickness 6.00 mm |
HB @Thickness 0.236 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 100 Hz |
3.4 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | in transformer oil; IEC 60243-1 |
| Dissipation Factor | 0.0010 @Frequency 100 Hz |
0.0010 @Frequency 100 Hz |
IEC 60250 |
| 0.014 @Frequency 1e+6 Hz |
0.014 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Food Compliance | yes | BGVV |
| yes | FD A |
Users viewing this material also viewed the following:
- MV Labs SM810 Sm2O3 Samarium oxide
- Lehmann & Voss LUVOCOM® 1-7177 Polyamide 66, with PTFE, lubricant modified, heat stabilized
- FloMet 430L Stainless Steel
- Kobe Steel KS15-3-3-3 Beta Titanium Alloy, AMS 4914, Solution treated
- Multibase Multi-Flex® A 8030 C2 Black TPE Thermoplastic Elastomer
- SABIC Innovative Plastics LNP THERMOCOMP JF002 PES (Asia Pacific)
- Lubrizol Estane® UB601 Thermoplastic Polyurethane
- 3M Scotch-Weld™ CA100 Instant Adhesive
- 3M 7603 Clear Vinyl Label Material
- Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet
Copyright © lookpolymers.com All Rights Reserved