SABIC Innovative Plastics ULTEM PW2100 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM PW2100 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber filled, standard flow Polyetherimide (Tg 217°C). Specific grade-colors are designed and certified for use in Potable Water applications. KTW, WRAS, ACS, NSF-61 and W270 certified. US FDA and European Food Contact approved.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.600 % | 0.600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 9.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 140 MPa | 20300 psi | ISO 2039-1 |
| Tensile Strength at Break | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 185 MPa | 26800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/2C |
| Taber Abrasion, mg/1000 Cycles | 15 | 15 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 26.0 µm/m-°C @Temperature 23.0 - 150 °C |
14.4 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 23.0 - 150 °C |
33.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 212 °C | 414 °F | Rate B/50; ISO 306 |
| 217 °C | 423 °F | Rate B/120; ISO 306 | |
| 223 °C | 433 °F | Rate A/50; ISO 306 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Oxygen Index | 46 % | 46 % | ISO 4589 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Teknor Apex Monprene® MP-1848R Thermoplastic Elastomer
- Chosun Refractories BCT-145 Acid-proof Castable
- Chi Mei Polylac® PA-777B ABS - High Heat
- Asahi Kasei Leona® TR160 Nylon 66
- Bapolene® 4022 Polypropylene, Biaxially Oriented Film Grade
- E-Polymers SEPAZ® LC30 PP Copolymer LFT Resin
- Ineos Nova 5460 High Impact Polystyrene (discontinued **)
- Solvay RHODAPEX® EST-30/SK Surfactant
- Styrolution Luran® SAN C Styrene Acrylonitrile
Copyright © lookpolymers.com All Rights Reserved