Beijing Chemical Industry KAIFA® 3030 PET Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® 3030 PET Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High mechanical strength, Creep resistant, Low frictionInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm |
559 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 240 - 260 °C | 464 - 500 °F | Injection Temp. |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 - 8 hour | 4 - 8 hour | |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
| Back Pressure | 8.00 - 18.0 MPa | 1160 - 2610 psi |
Users viewing this material also viewed the following:
- NEU NeuSoft™ 597-60A Industrial Ether TPU / SBC blend
- Polymer Resources NY6/12-G43 Nylon 612, 43% Glass Reinforced
- Multibase Multi-Flex® D 3902 MRS TPE Thermoplastic Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer (Asia Pacific)
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7330-9000 TPE
- SABIC Innovative Plastics NORYL GTX GTX8730 PPE+PA (Europe-Africa-Middle East)
- Loctite® 712 Isopropanol Base Surface Primer
- Latrobe Staminal™ Shock Resisting Die Steel
- BNZ Materials 2645LI Insulating Aggregate
Copyright © lookpolymers.com All Rights Reserved