BLUESTAR LXS 315 PPE-PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Unreinforced |
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BLUESTAR LXS 315 PPE-PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Applications: Spinning industrial partsInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Temperature 23.0 °C, Time 86400 sec |
0.10 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 300 °C |
12 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | type I; ASTM D638 |
| Elongation at Break | 25 % | 25 % | type I; ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 132G (SO) Synthetic Oil
- Polymax® Maxelast® P3740 TPE, PP Overmold or Standalone use
- Eastman P76CC PET (discontinued **)
- KB Alloys 6% Zirconium 4% Vanadium Aluminum Alloy
- H.C. Starck Amperit® 527.074 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17
- SABIC Innovative Plastics NORYL CTI2550 PPE+HIPS (Europe-Africa-Middle East)
- Fainplast Compounds PH 75/AS Flexible PVC, Transparent Extrusion
- M. Holland Company MAGMA® LM311-DX LLDPE (discontinued **)
- 3M Scotchcal™ 3632-76 Translucent Film
Copyright © lookpolymers.com All Rights Reserved