BASF Ultrason E 1010 PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | BASF |
| Trade Name | Ultrason E |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultrason E 1010 PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultrason E 1010 is an unreinforced, low viscosity injection molding PES grade. It flows readily and offers outstanding heat resistance and dimensional stability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 2.2 % | 2.2 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.80 % | 0.80 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 48 cm³/g | 48 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM Data; MD |
| Linear Mold Shrinkage, Flow | 0.0079 cm/cm | 0.0079 in/in | ISO Data |
| Linear Mold Shrinkage, Transverse | 0.0082 cm/cm | 0.0082 in/in | ISO Data |
| Melt Flow | 150 g/10 min @Load 10.0 kg, Temperature 360 °C |
150 g/10 min @Load 22.0 lb, Temperature 680 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 154 MPa | 22300 psi | ISO 2039-1 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5mm/min; ISO 527-2 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 6.7 % | 6.7 % | 5mm/min; ISO 527-2 |
| Elongation at Yield | 6.7 % | 6.7 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-2 |
| Shear Modulus | 0.200 GPa @Temperature 225 °C |
29.0 ksi @Temperature 437 °F |
ISO 6721 |
| 0.900 GPa @Temperature 200 °C |
131 ksi @Temperature 392 °F |
ISO 6721 | |
| 0.950 GPa @Temperature 100 °C |
138 ksi @Temperature 212 °F |
ISO 6721 | |
| 1.00 GPa @Temperature 50.0 °C |
145 ksi @Temperature 122 °F |
ISO 6721 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| Izod Impact, Unnotched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 2700 MPa | 392000 psi | elongation <0.5%, 23°C; ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
28.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| 59.0 µm/m-°C @Temperature 140 - 180 °C |
32.8 µin/in-°F @Temperature 284 - 356 °F |
ISO 11359-1/-2 | |
| Maximum Service Temperature, Air | 200 °C | 392 °F | short cycle operations |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-2 |
| Glass Transition Temp, Tg | 222 °C | 432 °F | ISO 11357-1/-2 |
| UL RTI, Electrical | 190 °C | 374 °F | 50% decrease of tensile strength after 20000h; 746B |
| Flammability, UL94 | V-1 @Thickness 1.60 mm |
V-1 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.65 | 1.65 | |
| Transmission, Visible | 88 % @Thickness 2.00 mm |
88 % @Thickness 0.0787 in |
ASTM D 1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.9 @Frequency 100 Hz |
3.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0017 @Frequency 100 Hz |
0.0017 @Frequency 100 Hz |
IEC 60250 |
| 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 125 V | 125 V | Test liquid A & B; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 340 - 390 °C | 644 - 734 °F | Injection molding |
| Mold Temperature | 140 - 180 °C | 284 - 356 °F | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding, Extrusion |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4121N (22401) Linear Low Density Polyethylene
- Arlon A4020-C004FR 0.020" (0.508 mm) Cured Fusible Silicone Rubber with Sinusoidal Fiberglass Substrate
- Lehmann & Voss LUVOCOM® 1301-8095 PPS, linear, with glass fiber
- Multibase Multi-Flex® TPE A 5501 LC GREY
- Heatbath/Park AL-3 High Speed Hardening Salt
- Styron CALIBREâ„¢ 701-10 Polycarbonate Resin
- Unifrax Fiberfrax® Duraboard® 3000 Ceramic Fiber Board
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Carbon Black, N-550 (FEF)
- Covestro Bayblend® T 85 MN Polycarbonate/ABS Blend
Copyright © lookpolymers.com All Rights Reserved