SABIC Innovative Plastics LNP LUBRICOMP UFL36SXC PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP UFL36SXC PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* UFL36SXC is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm @Time 86400 sec |
0.0017 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0082 cm/cm @Time 86400 sec |
0.0082 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 196 MPa | 28400 psi | ASTM D638 |
| 196 MPa | 28400 psi | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.5 % | 2.5 % | ISO 527 | |
| Tensile Modulus | 9.88 GPa | 1430 ksi | 1 mm/min; ISO 527 |
| 12.41 GPa | 1800 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| 286 MPa | 41500 psi | ISO 178 | |
| Flexural Modulus | 10.82 GPa | 1569 ksi | ASTM D790 |
| 11.23 GPa | 1629 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.14 J/cm | 19.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.49 | 0.49 | ASTM D3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Omni Plastics OmniLon™ 6 PA6 WF20 Mineral Filled Nylon
- MarkeTech Silicon Single Crystal Semiconductor Wafer, p-type, Boron Doped, Float Zone Grown
- Kinlead HSS13 Normal Grade Heat Sealable Film (thickness: 25 µm)
- Ineos ABS Lustran® H802
- Lucite International Diakon® ST45G6 Toughened Acrylic Polymer
- Green Dot Terratek® Flex GDH-B1 Compostable Bioplastic Elastomer
- A. Schulman POLYBATCH™ AC-20531L UV Absorber Concentrate
- CTC X-PRO TF 1120 HP Polypropylene Homopolymer, 20% Talc Filled
- Ascend Performance Materials Vydyne® R515 Nylon 66, 15% Glass Reinforced, Conditioned
- ATG s.r.l. EACM Ethylene-Acrylic Rubber
Copyright © lookpolymers.com All Rights Reserved