Sharadaa Ceramics VELECRETE RC 103 Rodding Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | VELECRETE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics VELECRETE RC 103 Rodding Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: The Rodding Castables offered by us are user friendly in nature and does not require high energy mixing machines and vibrators. Free flowing in nature, these castables are designed in compliance with international standards.Bond: UltrafineAggregate: Sintered MulliteType of Setting: HydraulicInformation provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.50 g/cc | 0.0903 lb/in³ | After Drying at 110°C |
| Porosity | 16 - 18 % @Temperature 1300 °C |
16 - 18 % @Temperature 2370 °F |
|
| Grain Size | <= 10000 µm | <= 10000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0130 GPa @Temperature 1000 °C |
1.89 ksi @Temperature 1830 °F |
Cold |
| 0.0150 GPa @Temperature 1100 °C |
2.18 ksi @Temperature 2010 °F |
Hot | |
| 0.0180 GPa @Temperature 1400 °C |
2.61 ksi @Temperature 2550 °F |
Cold | |
| 0.0180 GPa @Temperature 110 °C |
2.61 ksi @Temperature 230 °F |
Cold | |
| Compressive Strength | 65.0 MPa @Temperature 1000 °C |
9430 psi @Temperature 1830 °F |
Cold Crushing |
| 90.0 MPa @Temperature 110 °C |
13100 psi @Temperature 230 °F |
Cold Crushing | |
| 90.0 MPa @Temperature 1400 °C |
13100 psi @Temperature 2550 °F |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.63 W/m-K @Temperature 600 °C |
11.3 BTU-in/hr-ft²-°F @Temperature 1110 °F |
Hot Face |
| Maximum Service Temperature, Air | 1600 °C | 2910 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 60 % | 60 % | |
| Fe2O3 | 1.2 % | 1.2 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | <-0.7% | 1600°C |
| Thermal Expansion | 0.9 | at 1100°C |
| Thermal Shock Resistance | Excellent |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY XP4034 ASA+PC
- Techmer ES HiFill® PA6/6 GF33 L BKN001 33% Glass Filled (Conditioned)
- A. Schulman POLYFORT™ PP 3720
- Ensinger TECANYL™ MT CF30 Autoclavable Polymer
- 3A Composites Core Materials AIREX® C70.250 Universal Structural Foam
- Abatron AboCast 10-5/AboCure 3-4 Epoxy
Copyright © lookpolymers.com All Rights Reserved