BASF Ultramid® B3WG6 30% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3WG6 30% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Water Absorption 6.3 - 6.9 %
6.3 - 6.9 %
ISO 62
Moisture Absorption at Equilibrium 1.9 - 2.3 %
1.9 - 2.3 %
23°C/50% R.H.; ISO 62
Viscosity Test 140 cm³/g
140 cm³/g
Viscosity number; ISO 307
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
Melt Flow 68 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 68 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 185 MPa
26800 psi
50mm/min; ISO 527
Elongation at Yield 3.5 %
3.5 %
50mm/min; ISO 527
Modulus of Elasticity 9.50 GPa
1380 ksi
ISO 527
Flexural Strength 270 MPa
39200 psi
ISO 178
Flexural Modulus 8.60 GPa
1250 ksi
ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
ISO 180/A
Charpy Impact Unnotched 9.50 J/cm²
45.2 ft-lb/in²
ISO 179/1eU
8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
ISO 179/1eA
1.10 J/cm²

@Temperature -30.0 °C
 5.24 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 - 25.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 11.1 - 13.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 60.0 - 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 33.3 - 38.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-1/-2
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 145 °C
293 °F
for 50% loss of tensile strength after 20,000 hr
175 °C
347 °F
for 50% loss of tensile strength after 5,000 hr
200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.023

@Frequency 1.00e+6 Hz
 0.023

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 450 V
450 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat