BASF Ultramid® B3M6 30% Mineral Filled PA6 (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® B3M6 30% Mineral Filled PA6 (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid B3M6 is a 30% mineral reinforced injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent laser markability.

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	ISO 1183
Water Absorption	6.2 %	6.2 %	ISO 62
Moisture Absorption at Equilibrium	2.4 %	2.4 %	23°C/50% R.H.; ISO 62
Viscosity Test	150 cm³/g	150 cm³/g	Viscosity number
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	76.0 MPa	11000 psi	0.2 in/min; ASTM Test
Tensile Strength, Ultimate	85.0 MPa	12300 psi	5mm/min; ISO 527
Elongation at Break	5.0 %	5.0 %	0.2 in/min; ASTM Test
	15 %	15 %	5mm/min; ISO 527
Tensile Modulus	4.60 GPa	667 ksi	1mm/min; ISO 527
	5.17 GPa	750 ksi	ASTM Test
Flexural Modulus	4.00 GPa	580 ksi	ISO Data
	4.10 GPa	595 ksi	ASTM Test
Izod Impact, Notched	0.450 J/cm @Temperature -40.0 °C	0.843 ft-lb/in @Temperature -40.0 °F	ASTM Test
	0.640 J/cm @Thickness 3.17 mm	1.20 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	6.50 kJ/m²	3.09 ft-lb/in²	ISO Test
Charpy Impact Unnotched	22.0 J/cm²	105 ft-lb/in²	ISO 179
	14.5 J/cm² @Temperature -30.0 °C	69.0 ft-lb/in² @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	ISO 179
	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	30.0 µm/m-°C @Temperature -30.0 - 30.0 °C	16.7 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
CTE, linear, Parallel to Flow	65.0 µm/m-°C	36.1 µin/in-°F	ISO 11359
CTE, linear, Transverse to Flow	60.0 µm/m-°C	33.3 µin/in-°F	ISO 11359
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	195 °C	383 °F	ASTM Test
	195 °C	383 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	120 °C	248 °F	ASTM Test
	120 °C	248 °F	ISO 75
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Constant	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	IEC 60250
Dissipation Factor	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250
	0.020 @Frequency 100 Hz	0.020 @Frequency 100 Hz	IEC 60250
Comparative Tracking Index	450 V	450 V	IEC 60112

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat