- Polymer Resources PPX-GP3-WR Modified-PPO, Wear Resistant
Polymer Resources PPX-GP3-WR Modified-PPO, Wear Resistant
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX-GP3-WR Modified-PPO, Wear Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified-Polyphenylene Oxide, Wear Resistant, 235F HDTFeatures: • Hydrolytically Stable • Low to No Water Absorption • Good Wear ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 15 - 21 g/10 min @Load 11.6 kg, Temperature 250 °C |
15 - 21 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Break | 32 % | 32 % | ASTM D638 |
| Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 2.21 GPa | 320 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Temperature -30.0 °C |
2.50 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| 2.14 J/cm @Temperature 22.8 °C |
4.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | |
| Gardner Impact | 13.6 J | 10.0 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 243 - 293 °C | 470 - 560 °F | |
| Middle Barrel Temperature | 254 - 299 °C | 490 - 570 °F | |
| Front Barrel Temperature | 266 - 304 °C | 510 - 580 °F | |
| Melt Temperature | 274 - 302 °C | 525 - 575 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- MV Labs FE1050 (NH4)2Fe(SO4)2·6H2O Ammonium iron(II) sulfate hexahydrate
- Solvay Specialty Polymers EpiSpire® EP-340 Sulfone, High Temperature (HTS) (Unverified Data**)
- Honeywell Aegisâ„¢ H100ZP Nylon 6 Extrusion Grade Homopolymer Film
- Kostat E-2001 Conductive PP Compound
- SABIC Innovative Plastics LNP LUBRICOMP DL003E PC (Asia Pacific)
- Wellman Wellamid® MR409 22H-N 40% Mineral Reinforced Nylon 66, Heat Stabilized
- Dow Engage® 8440 Polyolefin Elastomer
- Arkema Group Orgalloy® RS 6630 Polyamide 6.6 Alloy 30% Glass Fiber reinforced
- Fluorocarbon Rubber (FPM), Low Temperature Grade
Copyright © lookpolymers.com All Rights Reserved