SABIC Innovative Plastics NORYL PX2801Z PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX2801Z PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+HIPS Unfilled FR V-0 100C
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 14.1 g/10 min @Load 10.0 kg, Temperature 250 °C |
14.1 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | SABIC - Japan Method |
| Elongation at Break | 40 % | 40 % | SABIC - Japan Method |
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 2.31 GPa | 335 ksi | ASTM D790 |
| Izod Impact, Notched | 2.15 J/cm | 4.03 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
UL 94 |
| V-0 @Thickness 1.20 mm |
V-0 @Thickness 0.0472 in |
UL 94 | |
| 5VB @Thickness 2.50 mm |
5VB @Thickness 0.0984 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.78 @Frequency 50.0 - 60.0 Hz |
2.78 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dissipation Factor | 0.0030 @Frequency 50.0 - 60.0 Hz |
0.0030 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Omni Plastics OmniLon™ 6 PA6 IM20 Unfilled/ Impact Modified Nylon
- Polykemi AB SCANTEC PC S60R GF30 Polycarbonate, Glass-Fiber Reinforced
- DSM Akulon® K223-HMS6 Nylon 6-30% Mineral Reinforced (European and Asian Grade) (Dry) (discontinued **)
- Lucent Polymers PC/ABS-FR0 Polycarbonate+ABS, Flame Resistant
- Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA), 33% Glass Fiber
- Hexcel® HexWeb® CR III 3/8-5052-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Dow INTEGRAL™ 909 Monolayer Adhesive Film / Automotive Headliners
Copyright © lookpolymers.com All Rights Reserved