BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3G8 BK00564 40% Glass Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3G8 BK00564 is a 40% glass filled, pigmented black, injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Water Absorption | 5.4 - 6.0 % | 5.4 - 6.0 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.6 - 2.0 % | 1.6 - 2.0 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307 |
| Melt Flow | 78.65 g/10 min @Load 5.00 kg, Temperature 275 °C |
78.65 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 205 MPa | 29700 psi | 50mm/min; ISO 527 |
| Elongation at Yield | 2.8 % | 2.8 % | 50mm/min; ISO 527 |
| Flexural Strength | 290 MPa | 42100 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | ISO 180/A |
| 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | ISO 179/1eU |
| 8.50 J/cm² @Temperature -30.0 °C |
40.5 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/1eA |
| 1.10 J/cm² @Temperature -30.0 °C |
5.24 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 10.0 - 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
5.56 - 8.33 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 55.0 - 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
30.6 - 38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 200 °C | 392 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.014 @Frequency 100 Hz |
0.014 @Frequency 100 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK00564 | |
| Commercial Status | North America and Europe | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- MV Labs DY400 DyCl3·6H2O Dysprosium chloride hexahydrate
- Plastcom SLOVAMID 6 GF 30 FRA 3 PA6, 30% glass fibre, flame retardant
- Palm Labs Adhesives Turbo Fuse Series 180 (2400 Viscosity) Rapid Bonding Adhesive
- Star Plastics PC/PET7901 Molding Grade PC/PET
- Teknor Apex Sinvicomp SGH 6500 Polyvinyl Chloride, Flexible
- Tra-Con Tra-Bond 2104 Rigid Epoxy Staking Compound
- CMW® ELKONITE® 7065 Infiltrated Molybdenum Silver contact material ASTM B662 Table 1, Class A1
- Solvay TECHNYL® A 216 V30 Natural FA PA66, 30% glass fiber, Conditioned
- M. Holland Company MAGMA® LM115-C LLDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved