Material Notes:
Ultramid A3WG5 is a 25% glass fiber reinforced and heat resistance injection molding PA66 grade.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Water Absorption 5.7 - 6.3 %
5.7 - 6.3 %
ISO 62
Moisture Absorption at Equilibrium 1.7 - 2.1 %
1.7 - 2.1 %
(23°C/50% R.H.); ISO 62
Viscosity Test 145 cm³/g
145 cm³/g
Viscosity number; ISO 307
Linear Mold Shrinkage 0.0055 cm/cm
0.0055 in/in
Melt Flow 198 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 198 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 120 MPa
17400 psi
50mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50mm/min; ISO 527
Modulus of Elasticity 6.50 GPa
943 ksi
ISO 527
Flexural Strength 200 MPa
29000 psi
ISO 178
Flexural Modulus 6.00 GPa
870 ksi
ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
ISO 180/A
Charpy Impact Unnotched 9.00 J/cm²
42.8 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 4400 MPa
638000 psi
ISO 899
4400 MPa
638000 psi
ISO 899-1
Thermal Properties Metric English Comments
Specific Heat Capacity 1.60 J/g-°C
0.382 BTU/lb-°F
Thermal Conductivity 0.340 W/m-K
2.36 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 260 °C
500 °F
DIN 53765
Maximum Service Temperature, Air 145 °C
293 °F
for 50% loss of tensile strength after 20,000 hr
175 °C
347 °F
for 50% loss of tensile strength after 5,000 hr
240 °C
464 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Constant 5.5

@Frequency 1.00e+6 Hz
 5.5

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.30

@Frequency 1.00e+6 Hz
 0.30

@Frequency 1.00e+6 Hz
 IEC 60250
0.30

@Frequency 100 Hz
 0.30

@Frequency 100 Hz
 IEC 60250
Comparative Tracking Index 450 V
450 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Injection-molding/Extrusion
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat