BASF Ultraform® N2650 Z2 (LEV) POM

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	BASF
Trade Name	Ultraform®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultraform® N2650 Z2 (LEV) POM.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Is a POM + PUR, elastomer-modified injection-molding grades with high impact strength for clips, snap and fastening elements, also for components subject to impact stress.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ISO 1183
Water Absorption	0.80 %	0.80 %	Saturation; ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	23°C; 50% RH; ISO 62
Melt Flow	8.5 g/10 min @Load 2.16 kg, Temperature 190 °C	8.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	105 MPa @Load 36.5 kg, Time 30.0 sec	15200 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Tensile Strength, Yield	52.0 MPa	7540 psi	50 mm/min; ISO 527-2
Elongation at Break	48 %	48 %	ISO 527-2
Elongation at Yield	13 %	13 %	ISO 527-2
Modulus of Elasticity	1.90 GPa	276 ksi	ISO 527-2
Izod Impact, Notched (ISO)	7.00 kJ/m² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	ISO 180/A
	10.0 kJ/m² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	ISO 180/A
Charpy Impact Unnotched	29.0 J/cm² @Temperature -30.0 °C	138 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	700 MPa	102000 psi	ISO 899-1

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	13.0 µm/m-°C @Temperature 23.0 - 55.0 °C	7.22 µin/in-°F @Temperature 73.4 - 131 °F	DIN 53752
Melting Point	167 °C	333 °F	DIN 53765
Maximum Service Temperature, Air	100 °C	212 °F
Deflection Temperature at 1.8 MPa (264 psi)	80.0 °C	176 °F	ISO 75-2
Vicat Softening Point	140 °C	284 °F	ISO 306

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	IEC 60093
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	IEC 60093
Dielectric Constant	3.9 @Frequency 1.00e+6 Hz	3.9 @Frequency 1.00e+6 Hz	IEC 60250
	4.1 @Frequency 100 Hz	4.1 @Frequency 100 Hz	IEC 60250
Dielectric Strength	34.0 kV/mm	864 kV/in	IEC 60243-1
Dissipation Factor	0.0080 @Frequency 100 Hz	0.0080 @Frequency 100 Hz	IEC 60250
	0.012 @Frequency 1.00e+6 Hz	0.012 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	Test solution A; IEC 60112
	600 V	600 V	Test solution B; IEC 60112

Processing Properties	Metric	English	Comments
Melt Temperature	190 - 215 °C	374 - 419 °F	Injection-molding
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F

Descriptive Properties	Value	Comments
Commercial Status	Europe
Primary Processing Technique	Injection Molding