LG Chemical NBR 6230 High Acrylonitrile Polymer
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical NBR 6230 High Acrylonitrile Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: NBR 6230 is a copolymer of butadiene and acrylonitrile manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 6230 is a non staining, low mooney, and medium high acrylonitrile polymer designed to aid in processing operations such as extruding and calendaring. NBR6230 is a low temperature polymerized polymer, and such as, retains the excellent processing and the good physical properties of a cold nitrile rubber. NBR 6230 is a low mooney version of NBR 6240.Applications: NBR 6230 is recommended to use in packings, shoe products, chemically blown sponge, oil field products, industrial and automotive molded parts. .CAS No: 9003-18-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.990 g/cc | 0.990 g/cc | |
| Volatiles | 0.30 % | 0.30 % | |
| Mooney Viscosity | 34 @Temperature 100 °C |
34 @Temperature 212 °F |
ML 1+4 |
| Ash | <= 0.50 % | <= 0.50 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 68 @Temperature 145 °C, Time 1190 sec |
68 @Temperature 293 °F, Time 0.330 hour |
Cured |
| 71 @Temperature 100 °C, Time 259000 sec |
71 @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging | |
| 45 @Treatment Temp. 25.0 °C, Time 259000 sec |
45 @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 68 @Treatment Temp. 100 °C, Time 259000 sec |
68 @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| 71 @Treatment Temp. 100 °C, Time 259000 sec |
71 @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| Tensile Strength at Break | 17.8 MPa @Temperature 145 °C, Time 1190 sec |
2580 psi @Temperature 293 °F, Time 0.330 hour |
Cured |
| 18.3 MPa @Temperature 100 °C, Time 259000 sec |
2650 psi @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging | |
| 27.0 MPa @Temperature 145 °C, Time 2990 sec |
3920 psi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 | |
| 12.9 MPa @Treatment Temp. 25.0 °C, Time 259000 sec |
1870 psi @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 18.1 MPa @Treatment Temp. 100 °C, Time 259000 sec |
2630 psi @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| 18.2 MPa @Treatment Temp. 100 °C, Time 259000 sec |
2640 psi @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| Elongation at Break | 396.5 % @Temperature 100 °C, Time 259000 sec |
396.5 % @Temperature 212 °F, Time 72.0 hour |
Circulating Oven Aging |
| 420 % @Temperature 145 °C, Time 1190 sec |
420 % @Temperature 293 °F, Time 0.330 hour |
Cured | |
| 590 % @Temperature 145 °C, Time 2990 sec |
590 % @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 | |
| 370 % @Treatment Temp. 25.0 °C, Time 259000 sec |
370 % @Treatment Temp. 77.0 °F, Time 72.0 hour |
Aged fuel C | |
| 394.5 % @Treatment Temp. 100 °C, Time 259000 sec |
394.5 % @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #1 Oil | |
| 398.5 % @Treatment Temp. 100 °C, Time 259000 sec |
398.5 % @Treatment Temp. 212 °F, Time 72.0 hour |
Aged ASTM D #3 Oil | |
| 300% Modulus | 0.0112 GPa @Temperature 145 °C, Time 2990 sec |
1.62 ksi @Temperature 293 °F, Time 0.830 hour |
cured; ASTM D412 |
| Rebound | 41 % @Temperature 30.0 °C |
41 % @Temperature 86.0 °F |
|
| Abrasion | 0.2815 | 0.2815 | AKRON |
| Compression Set | 22.5 % @Temperature 100 °C, Time 259000 sec |
22.5 % @Temperature 212 °F, Time 72.0 hour |
160°C x 30 min. Cured) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Bound AN Content | 0.34 | |
| Color | Tan | |
| Components | HAF (IRB#7) | 40 phr, ASTM D3187 |
| NBR 6230 | 100 phr, ASTM D3187 | |
| Stearic Acid | 1 phr, ASTM D3187 | |
| Sulfur | 1.5 phr, ASTM D3187 | |
| TBBS | 0.7 phr, ASTM D3187 | |
| ZnO | 3 phr, ASTM D3187 | |
| Compound Recipe | Antioxidant(3-C) | 1 phr |
| Antioxidant(RD) | 2 phr | |
| Carbon Black(SRF) | 80 phr | |
| CZ | 2 phr | |
| NBR 6230 | 100 phr | |
| Plasticizer(DOP) | 10 phr | |
| Stearic Acid | 1 phr | |
| Sulfur | 0.5 phr | |
| TT | 1 phr | |
| Zinc Oxide | 5 phr | |
| Rheometer | 1.1 min | ts1, 160°C x 12 min, 1° Arc, MDR |
| 1.2 lb-in | ML, 160°C x 12 min, 1° Arc, MDR | |
| 1.7 min | t'50, 160°C x 12 min, 1° Arc, MDR | |
| 2.7 min | t'90, 160°C x 12 min, 1° Arc, MDR | |
| 23.0 lb-in | MH, 160°C x 12 min, 1° Arc, MDR | |
| Volume Swell | -0.026 | Aged ASTM D #3 Oil (100°C x 72hrs) |
| -0.061 | Aged ASTM D #1 Oil (100°C x 72hrs) | |
| 0.405 | Aged fuel C (RT°C x 72hrs) |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA-81 UVA UV-Absorbing Acrylic Resin
- NOVA Chemicals Novapol® HP-Y353-A HDPE Pipe Coating Resin
- Advanced Elastomer Systems Trefsin® 3201-75 W305 Thermoplastic Rubber (discontinued **)
- Resinlab® CYNERGY CA6807 Adhesive
- Heatbath/Park Parcure 275 Rubber Cure Salt
- Styron MAGNUMâ„¢ 3416 SLG Acrylonitrile Butadiene Styrene (ABS) Resin
- ChevronTexaco Black Pearl® NLGI 0 Grease EP
- Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Dry)
- LNP Lubricomp® PDX-O-97635 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE Lubricant (discontinued **)&l
Copyright © lookpolymers.com All Rights Reserved