Amity Thermosets ATO 176 Phenolic Molding Organic and inorganic Filler, Compression Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets ATO 176 Phenolic Molding Organic and inorganic Filler, Compression Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:Heat resistant ( asbestos free )Good electric insulationLow shrinkageLow water absorptionMedium mechanical strengthNot suitable for high mechanical tensionColor-blackMedium flow Applications: Heat shields Oven knobs Toaster knobsCoffee machine baseThermal insulationSwitchgear components which ought to withstand heat (200 0C), etc. Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.44 - 1.53 g/cc	0.0520 - 0.0553 lb/in³	Molding; IS 867-1963
Apparent Bulk Density	0.690 - 0.720 g/cc	0.0249 - 0.0260 lb/in³	IS 867-1963
Water Absorption	0.20 - 0.30 %	0.20 - 0.30 %	IS 13411-1993
Linear Mold Shrinkage	0.0050 - 0.0065 cm/cm	0.0050 - 0.0065 in/in	Compression specimen; IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	42.0 - 58.0 MPa	6090 - 8410 psi	5 mm/min.; IS 867-1963
Shear Strength	55.0 - 70.0 MPa	7980 - 10200 psi	IS 867-1963
Izod Impact, Notched	0.250 - 0.350 J/cm	0.468 - 0.656 ft-lb/in	IS 13411-1992

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	>= 200 °C	>= 392 °F	2 hours

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.2e+10 - 1.0e+11 ohm-cm	3.2e+10 - 1.0e+11 ohm-cm	IS 3396-1979
Surface Resistance	3.2e+9 - 1.0e+10 ohm	3.2e+9 - 1.0e+10 ohm	IS 3396-1979
Dielectric Strength	4.00 - 5.50 kV/mm @Temperature 90.0 °C	102 - 140 kV/in @Temperature 194 °F	IS 2584-1963

Processing Properties	Metric	English	Comments
Mold Temperature	160 - 180 °C	320 - 356 °F
Injection Pressure	15.68 - 34.3 MPa	2274 - 4970 psi	Mold Pressure
Cure Time	0.783 - 0.917 min	0.0131 - 0.0153 hour	per mm
Shelf Life	12.0 Month	12.0 Month	10-25°C