Arlon 51981XA015 0.0150" Uncured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51981XA015 0.0150" Uncured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Interleave 1: 2.5 mil PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Style 7628 FiberglassSide 2: Uncured Silicone RubberInterleave 2: 2.5 mil PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 88.9 microns | 3.50 mil | Side 1; Arlon SQA-TMS-003 |
| 88.9 microns | 3.50 mil | Side 2; Arlon SQA-TMS-003 | |
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |
| 381 microns | 15.0 mil | Overall Thickness; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 74 | 74 | Silicone Property; Arlon SQA-TMS-014 |
| Tensile Strength | 5.78 MPa | 838 psi | Silicone Property; Arlon SQA-TMS-008 |
| Elongation at Break | 128 % | 128 % | Silicone Property; Arlon SQA-TMS-008 |
| Tear Strength | 15.6 kN/m | 89.0 pli | Die B; Silicone Property; Arlon SQA-TMS-029 |
| Peel Strength | 0.701 kN/m | 4.00 pli | Bond Strength (S2 to S2); Arlon SQA-TMS-011 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 204 °C | 400 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| Flammability, UL94 | V-0 | V-0 | ARLON SQA-TMS-019 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 32.9 kV/mm | 835 kV/in | Arlon SQA-TMS-020 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
| 1.50 min @Pressure 0.345 MPa, Temperature 121 °C |
0.0250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 21.1 °C |
6.00 Month @Temperature 70.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Grey | Product |
| Natural | Substrate | |
| Total Product Weight (oz/yd2) | 18.6 | Arlon SQA-TMS-025 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PRE-ELEC® ESD 6600 Static Dissipative Thermoplastic Compound
- SABIC Innovative Plastics Geloy XTWM200 ASA (Asia Pacific)
- Solvay Specialty Polymers Polymist® XPP 522 Polytetrafluoroethylene (PTFE)
- SABIC Innovative Plastics Xylex X8303CL PC+POLYESTER
- A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy
- Trelleborg Emerson & Cuming Stycast® E 1400 Two-Component General Purpose Encapsulant
- ATI Allegheny Ludlum Stainless Steel 334 (UNS S33400)
- Beijing Ranger Chem PBT-201-G20 272 Flame Retarding FR PBT
- Arlon 48B12R005 0.005" (0.127 mm) Cured Silicone Rubber with Fiberglass Substrate
- AIM 70In/30Pb Solder for Photonic Packaging
Copyright © lookpolymers.com All Rights Reserved