Sax Polymers SAXALEN PPH319FX21 Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXALEN PPH319FX21 Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXALEN PPH319FX21 is a unfilled Polypropylene - Homopolymer intended for injection molding. It has flame retardant properties and suitable to produce thin-walled parts.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | |
| Melt Flow | 26 g/10 min @Load 2.16 kg, Temperature 230 °C |
26 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527-1 |
| Elongation at Break | 6.0 % | 6.0 % | 50 mm/min; ISO 527-1 |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 35.0 MPa | 5080 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.20 GPa | 174 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Flammability, UL94 | V-2 | V-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- Orion Engineered Carbons CORAX® N 339 ASTM Carbon Black
- Pyrotek Pyrocast AR FINE Castable Refractory
- PolyOne Nymax™ NM 6600-44GF0001 White Polyamide 66 (Nylon 66)
- Global Atron 6601-B General Purpose Nylon 66
- SABIC Innovative Plastics LNP Thermocomp FF008L PE
- Chevron Phillips MarFlex® 1013 LDPE Extrusion Coating Resin
- ExxonMobil Escorene™ UL 00014 Ethylene Vinyl Acetate Copolymer (European Grade)
- Braskem LL4800N PEBDL Cast Film Extrusion Polyethylene Copolymer
- Alliance Polymers Zythane™ 6080A Thermoplastic Polyurethane Elastomer
- Styrolution Luran® VLN SAN
Copyright © lookpolymers.com All Rights Reserved