SABIC Innovative Plastics Valox® 195 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 195 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PELLET FORM. For compounding only (not for injection molding). Unreinforced PBT. Melt viscosity between 740 and 900 poise. Natural Color (1001) Only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm |
0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.015 - 0.023 cm/cm @Thickness 2.30 - 4.60 mm |
0.015 - 0.023 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.017 cm/cm @Thickness 0.750 - 2.30 mm |
0.010 - 0.017 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.016 - 0.024 cm/cm @Thickness 2.30 - 4.60 mm |
0.016 - 0.024 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 17.9 % | 17.9 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.39 GPa | 347 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 18.5 J/cm | 34.7 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 139 µm/m-°C @Temperature 60.0 - 138 °C |
77.2 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 128 °C @Thickness 6.40 mm |
262 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C @Thickness 6.40 mm |
120 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.76cm^3/g | ASTM D792 |
Users viewing this material also viewed the following:
- RheTech Products GC30P200-01UV 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, Black
- Polykemi AB POLYfill PP CIP15015 Polypropylene, Mineral Reinforced
- SABIC Innovative Plastics LNP LUBRILOY UX98388 PPA
- Samsung Cheil Industries Infino® CF-1030 PC, Unreinforced High Impact
- SABIC Innovative Plastics NORYL GTX GTX678 PPE+PA (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ PP 3701
- Elektro-Isola Etronit IV Phenolic, Paper Reinforcement, Yellow, Sheets
- Dow Nordel® NDR 46140.01 EPDM Hydrocarbon Rubber
- Momentive Performance Materials GPC Boron Nitride (BN) Water Based Coating
- Techmer ES HiFill FR® PBT GF15 FR X 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved