BASF Capron® 8202C HS Nylon 6 (Dry)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® 8202C HS Nylon 6 (Dry)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Capron 8202C HS is a heat stabilized, low viscosity, polyamide 6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in non-heat stabilized (Capron 8202C) and/or pigmented versions.Capron 8202C HS is generally recommended for applications such as gears, valves, fittings, insulators, bushings, slides, window hardware, wiring devices, textile components and furniture casters. ASTM Callout PA242.Data provided by Allied Signal.Processing: Max. water content 0.25%. Product is supplied in sealed containers and drying is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 85°C (185 °F). Is recommended. Drying time is dependent on moisture level.Melt Temperature: 240-280 degC (464-536 degF). Mold Temperature: 80-95 degC (176-203 degF). Injection and Packing Pressure: 35-125 bar (500-1500psi) A mold temperature of 80-95 degC (176-203 degF) is recommended, but temperatures of as low as 10 degC (50 degF) can be used where applicable. Injection pressure controls the filling of the part and should be applied for 90% of ram travel. Packing pressure affects the final part and can be used effectively in controlling sink marks and shrinkage. It should be applied and maintained until the gate area is completely frozen off. Fast fill rates are recommended to insure uniform melt delivery to the cavity and prevent premature freezing. Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO data
Water Absorption 1.6 %
1.6 %
24 hrs; ISO data
Moisture Absorption at Equilibrium 2.6 %
2.6 %
50% RH; 23°C; ISO data
Water Absorption at Saturation 9.3 %
9.3 %
in water; 23°C; ISO data
Viscosity Measurement 48
48
Formic Acid Viscosity; ISO data
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM data MD
0.012 cm/cm
0.012 in/in
ISO data
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO Data
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 90.0 MPa
13100 psi
ASTM data at 5 mm/min.
Tensile Strength, Yield 90.0 MPa
13100 psi
50 mm/min; Same value from ASTM and ISO test.
Elongation at Break 10 %
10 %
Nominal
12 %
12 %
Nominal
Elongation at Yield 4.0 %
4.0 %
ASTM Value at 50 mm/min.
4.0 %
4.0 %
ISO Value at 50 mm/min.
Tensile Modulus 3.76 GPa
545 ksi
same value from ASTM and ISO test.
Flexural Yield Strength 110 MPa
16000 psi
ASTM Data
Flexural Modulus 3.17 GPa
460 ksi
ASTM Data
Poissons Ratio 0.35
0.35
ISO data
Shear Modulus 1.40 GPa
203 ksi
calculated
Coefficient of Friction 0.16
0.16
vs. steel.
0.33
0.33
vs. polymer
Coefficient of Friction, Static 0.24
0.24
vs. steel.
0.53
0.53
vs. polymer
Thermal Properties Metric English Comments
CTE, linear 81.0 µm/m-°C

@Temperature 20.0 °C
45.0 µin/in-°F

@Temperature 68.0 °F
ASTM data
Melting Point 220 °C
428 °F
ASTM and ISO test
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Value for both ASTM and ISO data.
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
ASTM Data
75.0 °C
167 °F
ISO data
Flammability, UL94 V-2

@Thickness 0.700 mm
V-2

@Thickness 0.0276 in
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
ISO data
Dielectric Strength 30.0 kV/mm
762 kV/in
ISO data
Comparative Tracking Index 600 V
600 V
ISO data
Processing Properties Metric English Comments
Processing Temperature 260 °C
500 °F
See Materials Notes
Mold Temperature 80.0 °C
176 °F
See Materials Notes
Drying Temperature 85.0 °C
185 °F
See Materials Notes