SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF00AH PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RF00AH is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this grade is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0037 cm/cm @Time 86400 sec |
0.0037 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.011 - 0.013 cm/cm @Time 86400 sec |
0.011 - 0.013 in/in @Time 24.0 hour |
ASTM D955 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 166 MPa | 24100 psi | ASTM D638 |
| 182 MPa | 26400 psi | ISO 527 | |
| Elongation at Break | 7.8 % | 7.8 % | ASTM D638 |
| 8.1 % | 8.1 % | ISO 527 | |
| Tensile Modulus | 17.23 GPa | 2499 ksi | 50 mm/min; ASTM D638 |
| 17.81 GPa | 2583 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 262 MPa | 38000 psi | ASTM D790 |
| 265 MPa | 38400 psi | ISO 178 | |
| Flexural Modulus | 14.47 GPa | 2099 ksi | ASTM D790 |
| 14.9 GPa | 2160 ksi | ISO 178 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.39 J/cm | 17.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 51.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 52.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 21.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 243 °C @Thickness 3.20 mm |
469 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ PS-30CF/10T 2S Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced, PTFE/Silicone Lubricated
- Northstar Polymers MPG-D70A Room-Temperature-Curable Polyurethane Casting Elastomer
- Lehmann & Voss LUVOCOM® 1500-0871 Polysulfone, with glass spheres
- LyondellBasell Petrothene® NA345184 Low Density Polyethylene (Film Extrusion)
- Industeel CLC 1.2316 Prehardened (300HB) and Corrosion Resistant Mold Steel
- ELASTO UK Dryflex® 8010-102 Flame Retardant TPE for Extrusion, Pebble Gray
- Alliance Polymers Viprene™ G90A-32U-BLK Thermoplastic Vulcanizate Elastomer
- BASF Lupranate® MS/264 Isocyanate
Copyright © lookpolymers.com All Rights Reserved