Ascend Performance Materials Vydyne® M344 Nylon 66/6, ignition resistant, Conditioned

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced
Manufacturer	Ascend Performance Materials (formerly Solutia)
Trade Name	VYDYNE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ascend Performance Materials Vydyne® M344 Nylon 66/6, ignition resistant, Conditioned.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Vydyne® M344 is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016”) thick.Availability:Asia PacificEuropeNorth AmericaAdditive:HalogenLubricantFeatures:DuctileGood Mold ReleaseHalogenatedIgnition ResistantLow DensityLubricatedUses:AppliancesAutomotive ElectronicsBobbinsConnectorsElectrical HousingElectrical PartsElectrical/Electronic ApplicationsFastenersIndustrial ApplicationsLighting ApplicationsLiving HingesPrinted Circuit BoardsSwitchesAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend

Physical Properties	Metric	English	Comments
Specific Gravity	1.27 g/cc	1.27 g/cc	ISO 1183
Water Absorption	0.80 %	0.80 %	24 hrs; ISO 62
Moisture Absorption at Equilibrium	1.9 %	1.9 %	Equilibrium at 50%rh; ISO 62
Linear Mold Shrinkage	0.013 cm/cm @Thickness 2.00 mm	0.013 in/in @Thickness 0.0787 in	ISO 294-4
Linear Mold Shrinkage, Transverse	0.018 cm/cm @Thickness 2.00 mm	0.018 in/in @Thickness 0.0787 in	ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	40.0 MPa	5800 psi	ISO 527-2
Elongation at Break	75 %	75 %	ISO 527-2
Elongation at Yield	25 %	25 %	ISO 527-2
Tensile Modulus	2.30 GPa	334 ksi	ISO 527-2
Flexural Strength	43.0 MPa	6240 psi	ISO 178
Flexural Modulus	1.40 GPa	203 ksi	ISO 178