Huntsman AVALON® 90 AKU Thermoplastic Polyurethane

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer Huntsman Corporation
Trade Name Avalon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman AVALON® 90 AKU Thermoplastic Polyurethane.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Introduction: AVALON 90 AKU is a part of the AVALON Crystal Range and offers a specially designed, flexible material wit a higher degree of transparency compared with conventional TPU at the same hardness. AVALON Crystal materials are particularly suitable for the sporting goods and fashion markets. It is recommended that a suitable UV stabilizer be incorporated for most applications to prevent premature yellowing. The features offered include:UV resistanceTransparencyDurabilityPhthalate free TPU Information provided by Alliance Polymers
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
ISO 2781
Mechanical Properties Metric English Comments
Hardness, Shore A 90
90
ISO 868
Hardness, Shore D 44
44
ISO 868
Tensile Strength at Break 45.0 MPa
6530 psi
ISO 37
Elongation at Break 450 %
450 %
ISO 37
100% Modulus 0.00800 GPa
1.16 ksi
ISO 37
300% Modulus 0.0160 GPa
2.32 ksi
ISO 37
Tear Strength 110 kN/m
628 pli
ISO 34B
Abrasion 50
50
mm<sup>3</sup>; ISO 4649
Processing Properties Metric English Comments
Feed Temperature 25.0 - 35.0 °C
77.0 - 95.0 °F
Rear Barrel Temperature 195 - 205 °C
383 - 401 °F
Middle Barrel Temperature 205 - 215 °C
401 - 419 °F
Front Barrel Temperature 210 - 220 °C
410 - 428 °F
Nozzle Temperature 205 - 215 °C
401 - 419 °F
Mold Temperature 25.0 - 50.0 °C
77.0 - 122 °F
Injection Pressure 2.00 - 10.0 MPa
290 - 1450 psi
Hold Pressure 1.00 - 5.00 MPa
145 - 725 psi
Back Pressure 0.0300 - 0.300 MPa
4.35 - 43.5 psi
Screw Speed 20 - 80 rpm
20 - 80 rpm
Descriptive Properties Value Comments
Compression Ratio 2-3:1
L/D Ratio 20-25:1
Ross Flex -10°C, BS 5131
Typical Screw Diameter 40-120 nm
Copyright © lookpolymers.com All Rights Reserved