- Rogers Corporation RO3010 Ceramic-Filled PTFE Composite, High Frequency Circuit Material
Rogers Corporation RO3010 Ceramic-Filled PTFE Composite, High Frequency Circuit Material
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Glass Filled, Molded |
| Manufacturer | Rogers Corporation |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Rogers Corporation RO3010 Ceramic-Filled PTFE Composite, High Frequency Circuit Material.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features and Benefits:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.80 g/cc | 0.101 lb/in³ | |
| Water Absorption | <= 0.10 % | <= 0.10 % | D24/23; IPC-TM-2.4.8 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 1.50 GPa | 218 ksi | X, Y-Direction; ASTM D638 |
| Peel Strength | 1.65 kN/m | 9.40 pli | Copper; 1/2 oz. EDC After Solder Float; IPC-TM-650 2.4.8 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 µm/m-°C @Temperature -55.0 - 288 °C |
6.11 µin/in-°F @Temperature -67.0 - 550 °F |
Y-Direction; ASTM D3386-94 |
| 13.0 µm/m-°C @Temperature -55.0 - 288 °C |
7.22 µin/in-°F @Temperature -67.0 - 550 °F |
X-Direction; ASTM D3386-94 | |
| 16.0 µm/m-°C @Temperature -55.0 - 288 °C |
8.89 µin/in-°F @Temperature -67.0 - 550 °F |
Z-Direction; ASTM D3386-94 | |
| Specific Heat Capacity | 0.800 J/g-°C | 0.191 BTU/lb-°F | Calculated |
| Thermal Conductivity | 0.950 W/m-K @Temperature 80.0 °C |
6.59 BTU-in/hr-ft²-°F @Temperature 176 °F |
Z Direction; ASTM C518 |
| Decomposition Temperature | 500 °C | 932 °F | TGA; ASTM D3850 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Cond. A; IPC 2.5.17.1 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | Cond. A; IPC 2.5.17.1 |
| Dielectric Constant | 9.9 - 10.5 @Frequency 1.00e+10 Hz |
9.9 - 10.5 @Frequency 1.00e+10 Hz |
Clamped stripline, Z-direction; IPC-TM-650 2.5.5.5 |
| 11.2 @Frequency 8.00e+9 - 4.00e+10 Hz |
11.2 @Frequency 8.00e+9 - 4.00e+10 Hz |
Differential Phase Length Method, Z-Direction | |
| Dissipation Factor | 0.0022 @Frequency 1.00e+10 Hz |
0.0022 @Frequency 1.00e+10 Hz |
IPC-TM-650 2.5.5.5 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Dimensional Stability | 0.5 mm/m | ASTM D257, Cond. A; X, Y-direction |
| Thermal Coefficient of Dielectric Constant | -280 ppm/°C | IPC-TM-650 2.5.5.5; 10 GHz; 0°C to 100°C; Z-Direction |
Users viewing this material also viewed the following:
- NOVA Chemicals Dylark® 378P20 High Performance Glass Filled Styrenic
- Indium Corp. Indalloy® 261 Bismuth-Silver Solder Alloy
- Multibase Multi-Flex® TEA 4001-35 Natural TPO Thermoplastic Polyolefin Elastomer
- Henkel Hysol EA 9696 Film Adhesive
- Polyram PlusTek PD300G4 Nylon 12, 20% Glass Fiber
- ExxonMobil Bicor™ 25ICT OPP Film
- Dow SiLK™ I 550 Semiconductor Dielectric Resin
- Ascend Performance Materials Vydyne® 41 NT Nylon 66, Impact Modified, DAM
- Garlock BLUE-GARD® 3200 Compressed Aramid Fiber Gasketing, SBR Binder
- Dielectric Polymers NT-988 High Tack Laminating Adhesive (discontinued **)
Copyright © lookpolymers.com All Rights Reserved