Aclo Accutech Polyethylene HD0232G20CV High Density Glass Reinforced Chemically Coupled
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Glass fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polyethylene HD0232G20CV High Density Glass Reinforced Chemically Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Approved to GMP.PE.018 Black A12438
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Melt Flow | 0.20 g/10 min | 0.20 g/10 min | ASTM D1238 |
| Ash | 18 - 22 % | 18 - 22 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 75 | 75 | ASTM D785 |
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.499 GPa | 362.5 ksi | ASTM D638 |
| Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
| Flexural Modulus | 2.499 GPa | 362.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F |
Users viewing this material also viewed the following:
- PolyOne Nanoblend™ MB 1201 Polypropylene Impact Copolymer (PP Impact Copolymer)
- Park Electrochemical Nelco® N4000-7 SI® FR-4 Epoxy Laminate and Prepreg
- Parker Chomerics CHO-BOND 1053, Part C Silicone Rubber
- SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6
- Lehmann & Voss LUVOCOM® 1100-7890 Polyether sulfone, with carbon fiber
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- CP-Polymer-Technik Wellamid® 6600 GV 30 HWCP 30% Glass Fiber Nylon 66, Heat Stabilized, Dry
- Chosun Refractories MF-2 Blast Furnace Tap-Hole Refractory
- Arkema Group Lucalor® RB 8065 CPVC, Pipe Grade
Copyright © lookpolymers.com All Rights Reserved