Lucite International Diakon® CLG902L Acrylic Polymer
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® CLG902L Acrylic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 7.3 g/10 min | 7.3 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 92 | 92 | ISO 2039-2 |
| Ball Indentation Hardness | 180 MPa | 26100 psi | ISO 2039-1 |
| Tensile Strength | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.80 kJ/m² | 0.857 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179/1eA |
| 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 71.0 µm/m-°C | 39.4 µin/in-°F | ASTM E831 |
| Vicat Softening Point | 102 °C | 216 °F | ISO 306B |
| 108 °C | 226 °F | ISO 306A | |
| Heat Distortion Temperature | 97.0 °C | 207 °F | ISO 75A |
| 100 °C | 212 °F | ISO 75B | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 0.40 % | 0.40 % | ASTM D1003 |
| Transmission, Visible | 92 % | 92 % | ASTM D1003 |
Users viewing this material also viewed the following:
- PolyOne Geon™ HC 2165G Polyvinyl Chloride, Flexible (PVC, Flexible)
- LTL Color Compounds ColorRxâ„¢ PE2-0201A Antimicrobial HDPE
- Henkel Turco EA Stripper 6930 Paint Remover
- LG Chemical 401 AF Flame Retardant HIPS
- Sanyo PELESTAT® 2450 Antistatic Additive
- SABIC Innovative Plastics NORYL HNA055 PPE+HIPS (Europe-Africa-Middle East)
- Total PSC 1450N High Heat Resistance Polystyrene
- ExxonMobil Bicor™ 70 MB OPP Film
- BASF Novolen® 3236 MC Polypropylene
- BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved