Asahi Kasei Tenac® LA543 Homopolymer Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Asahi Kasei |
| Trade Name | Tenac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Tenac® LA543 Homopolymer Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent friction and wear on metals and plastics, except POM.Information provided by Asahi Kasei Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | Asahi Kasei Method |
| Melt Flow | 14 g/10 min | 14 g/10 min | ISO 1133 D |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 - 1 & - 2 |
| Elongation at Break | 40 % | 40 % | ISO 527 - 1 & - 2 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527 - 1 & - 2 |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 / 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 -1 & -2 flat |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 -1 & -2 flat |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF30 - PP Homopolymer Polypropylene, 30% Long Carbon Fiber Reinforced
- PolyOne Versaflex™ CL E95 Thermoplastic Elastomer (TPE)
- Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK) (Unverified Data**)
- Victrex® Vicote® 708 Polyetheretherketone (PEEK) Powder
- Fujipoly Industries Zebra® 2005 Carbon Solid Self-Supported Connectors
- Chase Plastics CP Pryme® N100HL (Dry) Nylon 6, Heat Stabilized, Lubricated
- Wellman Wellamid® FRGF25-66 NBK3 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant
- Arlon LW201B##-P2 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported)
- DuPont Performance Polymers Zytel® HTN 54G35EF NC010 Polyphthalamide (PPA)
- Fibre Glast RAE 2426 / 2177 Epoxy (discontinued **)
Copyright © lookpolymers.com All Rights Reserved