Tra-Con Tra-Bond FS152C Clear Low Viscosity Epoxy Adhesive
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Tra-Con, Inc. |
| Trade Name | Tra-Bond |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tra-Con Tra-Bond FS152C Clear Low Viscosity Epoxy Adhesive.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRA-BOND FS152C is a low viscosity epoxy system containing no solvents, cures at room temperature and has excellent flow and wetting characteristics. This two-part adhesive mixes easily and develops strong, durable, tough bonds to most clean, dry material surfaces including metals, ceramics, glass, wood and many plastics. Its low viscosity readily facilitates bubble release and degassing, and it has a surface dry time of 6 hours at room temperature. Information provided by Tra-Con Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | Mixed |
| Solids Content | 100 % | 100 % | Reactive Solids Content |
| Viscosity | 700 cP @Temperature 25.0 °C |
700 cP @Temperature 77.0 °F |
After mixing |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 76 | 76 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 58.0 µm/m-°C @Temperature 20.0 °C |
32.2 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.0 @Frequency 1000 Hz |
4.0 @Frequency 1000 Hz |
|
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | |
| Dissipation Factor | 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 240 min @Temperature 65.0 °C |
4.00 hour @Temperature 149 °F |
|
| 4320 min @Temperature 25.0 °C |
72.0 hour @Temperature 77.0 °F |
||
| Pot Life | 60 min | 60 min |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear | |
| Mix Ratio, parts by weight | 100/30 | Resin/Hardener |
Users viewing this material also viewed the following:
- Piezo Kinetics 406 Lead Zirconate Titanate Piezoelectric
- Lehmann & Voss LUVOCOM® 80-8318-1 Polyacetal-copolymer, with PTFE, easy flowing
- LG Chemical M-Xylene
- Techmer ES HiFill FR® TPX-PBT-01006 40% Glass/Ceramic Filled
- SSAB Tunnplat Aluzink 260A RP-X High-strength Metal-coated Steel
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.002" thick)
- SABIC Innovative Plastics LNP THERMOTUF VF1001S Super Tough Nylon
- EMS-Grivory Grivory® TSS/2 FA PA666
- 3M 1532 Sandblast Stencil
- Teknor Apex Monprene® MP-2579B Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved