Arlon R37908R015L Silicone Rubber/Fiberglass/Acrylic/Polyester

Category Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon R37908R015L Silicone Rubber/Fiberglass/Acrylic/Polyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Laminated film: aluminized PEN; Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2, layer 1: acrylic PSA; Side 2, layer 2: polyester substrate; Side 2, layer 3: acrylic PSA; Interleave: Release substrate
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
silicone property; Arlon SQA-TMS-024
Thickness 25.4 microns
1.00 mil
laminated film; Arlon SQA-TMS-003
25.4 microns
1.00 mil
side 2 layer 2; Arlon SQA-TMS-003
31.8 microns
1.25 mil
side 2 layer 3; Arlon SQA-TMS-003
31.8 microns
1.25 mil
side 2 layer 1; Arlon SQA-TMS-003
63.5 microns
2.50 mil
side 1; Arlon SQA-TMS-003
203 microns
8.00 mil
substrate; Arlon SQA-TMS-003
381 microns
15.0 mil
overall; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 44
44
silicone property; ASTM D2240
Tensile Strength, Ultimate 7.58 MPa
1100 psi
silicone property; ASTM D412
Elongation at Break 650 %
650 %
silicone property; ASTM D412
Adhesive Bond Strength 0.0103 MPa
1.50 psi
adhesion to Al initially; Arlon SQA-TMS-011
0.0172 MPa
2.50 psi
adhesion to Al at 24 hours; Arlon SQA-TMS-011
0.0276 MPa
4.00 psi
adhesion to Al at 72 hours; Arlon SQA-TMS-011
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 160 °C
320 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Processing Properties Metric English Comments
Shelf Life 12.0 Month

@Temperature 23.9 °C
12.0 Month

@Temperature 75.0 °F
Descriptive Properties Value Comments
Color Silver