Arlon R36772R008 0.008" (0.203 mm) Fully Cured, Unsupported, Silicone Rubber with Fiberglass Substrate (

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon R36772R008 0.008" (0.203 mm) Fully Cured, Unsupported, Silicone Rubber with Fiberglass Substrate (.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Fully Cured, Unsupported, Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place of, material specificationsInformation provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.29 g/cc	0.0466 lb/in³	Compound Property; Arlon SQA-TMS-024
Thickness	38.1 microns	1.50 mil	Polyethylene, Interleave
	81.3 microns	3.20 mil	PTFE Coated Fiberglass, Substrate
	203 microns	8.00 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	45	45	Compound Property; ASTM D2240
Tensile Strength	5.52 MPa	800 psi	Compound Property; ASTM D412
Tensile Strength, Yield	1.38 MPa @Strain 100 %	200 psi @Strain 100 %	Compound Property; Arlon SQA-TMS-008
Elongation at Break	350 %	350 %	Compound Property; ASTM D412
Tear Strength	7.89 kN/m	45.0 pli	Die B, Compound Property; ASTM D624

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Processing Properties	Metric	English	Comments
Shelf Life	60.0 Month @Temperature 21.1 °C	60.0 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	8.1	Arlon SQA-TMS-025

Users viewing this material also viewed the following: