Arlon 51866R015E 0.0150" Cured/Uncured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51866R015E 0.0150" Cured/Uncured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Cured Silicone RubberSubstrate: Style 7628 FiberglassSide 2: Uncured Silicone RubberInterleave: 3 mil PEThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 |
| 127 microns | 5.00 mil | Side 2; Arlon SQA-TMS-003 | |
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |
| 381 microns | 15.0 mil | Overall Thickness; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | Silicone Property; ASTM D2240 |
| Tensile Strength | 4.83 MPa | 700 psi | Silicone Property; ASTM D412 |
| Elongation at Break | 200 % | 200 % | Silicone Property; ASTM D412 |
| Peel Strength | 0.877 kN/m | 5.00 pli | Bond Strength; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 200 °C | 392 °F | File E54153 |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | File E54153 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 27.6 kV/mm | 700 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 15.9 | Arlon SQA-TMS-025 |
Users viewing this material also viewed the following:
- Chevron Phillips 4518 LDPE Extrusion Coating Resin (discontinued **)
- Eastman 18DOA Polyethylene (discontinued **)
- Mitsubishi Xantar® FC 23 R Polycarbonate
- Techmer ES HiFill® PA6/6 GF33 NAT001 Y 33% Glass Filled (Conditioned)
- Teknor Apex Monprene® MP 1225 Thermoplastic Elastomer
- A. Schulman PAPERMATCH® T-4228-50 Specialty Masterbatch
- Elmer's Products Aron Alpha® 241 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- ArcelorMittal Dual Phase 600 Very high strength steel, Cold Rolled Steel
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 50% Cold Rolled (UNS S30200)
- Termopol Termoton® K2GA2060A TPE Compound, based on SEBS and Polyolefins
Copyright © lookpolymers.com All Rights Reserved