- Aclo Accutech Polypropylene Homopolymer HP0336M30CL Mica Reinforced Coupled
Aclo Accutech Polypropylene Homopolymer HP0336M30CL Mica Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336M30CL Mica Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 68 | 68 | ASTM D785 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.699 GPa | 536.5 ksi | ASTM D638 |
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Flexural Modulus | 3.900 GPa | 565.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.411 J/cm | 0.770 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 69 GF 40 Polypropylene Homopolymer, 40% Glass Fiber
- NIZHNEKAMSKNEFTEKHIM PE 4026Z (26460) Linear Low Density Polyethylene
- NOVA Chemicals Dylark® 250P20 High Performance Glass Filled Styrenic
- Inno-Comp INNOPOL® CS 1-5120 BLH 20% Talc-Filled Polypropylene Homopolymer
- Kraton® NEXAR™ MD9150 Polymer Barrier Membrane
- Westlake EF796 Low Density Polyethylene
- Plastics Group Polifil® GFPC-40 40% Glass-Reinforced Polycarbonate
- Polyplastics Duranex® 3116 Polybutylene Terephthalate (PBT), Standard, FR, UL approved regrind 50%, 7.5% GF filled
- Arlon CLTE-AT Commercial Ceramic PTFE
- 3M Scotch® 8916 Filament Tape
Copyright © lookpolymers.com All Rights Reserved