Arlon 51228R015 Silicone Rubber/Fiberglass Laminate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51228R015 Silicone Rubber/Fiberglass Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Interleave: 1.5 mil PE; Side 1, layer 2: uncured silicone rubber; Side 1, layer 1: Cured silicone rubber; Substrate: 7628 fiberglass; Side 2: cured silicone rubber
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | silicone property; Arlon SQA-TMS-024 |
| Thickness | 19.0 microns | 0.750 mil | side 1, layer 1 cured silicone; Arlon SQA-TMS-003 |
| 19.0 microns | 0.750 mil | side 2 silicone; Arlon SQA-TMS-003 | |
| 152 microns | 6.00 mil | side 1, layer 2 uncured silicone; Arlon SQA-TMS-003 | |
| 203 microns | 8.00 mil | substrate; Arlon SQA-TMS-003 | |
| 394 microns | 15.5 mil | overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 | 50 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 6.07 MPa | 880 psi | silicone property; ASTM D412 |
| Elongation at Break | 470 % | 470 % | silicone property; ASTM D412 |
| Adhesive Bond Strength | 0.0552 MPa | 8.00 psi | ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
|
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® BFL2000U PC (Asia Pacific)
- Lehmann & Voss LUVOCOM® 1105-8157 PEEK, with CNT
- SABIC Innovative Plastics Valox® IQ420 PBT
- SABIC Innovative Plastics Valox® V2105U PBT
- SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-LOY KX96821 Acetal
- A. Schulman CP775-01 Molding Grade, Low Density Polyethylene
- Ter Hell Plastic Terez® PBT 6750 T Polybutylene Terephthalate, Impact Modified
- Fainplast Compounds PHS 75/B Flexible PVC, Transparent Extrusion
- ACC QM 122 QSI Quantum Silicones 22 Durometer Condensation Cured Moldmaking Material
Copyright © lookpolymers.com All Rights Reserved