Arlon 30400N060 0.060" (1.52 mm) Uncured Silicone Rubber

Category	Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 30400N060 0.060" (1.52 mm) Uncured Silicone Rubber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Interleave 1: KodacelProduct: Uncured Silicone Rubber Interleave 2: Polyethylene Appearance: Translucent silicone rubber on polymer linerThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	76.2 microns	3.00 mil	Polyethylene Interleave
	127 microns	5.00 mil	Kodacel Interleave
	1520 microns	60.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	55	55	Silicone Property; ASTM D2240
Tensile Strength	8.96 MPa	1300 psi	Silicone Property; ASTM D412
Elongation at Break	700 %	700 %	Silicone Property; ASTM D412
Tear Strength	>= 35.1 kN/m	>= 200 pli	Silicone Property; ASTM D624
Compression Set	<= 28 %	<= 28 %	Silicone Property; ASTM D395

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Processing Properties	Metric	English	Comments
Cure Time	30.0 min @Temperature 177 °C	0.500 hour @Temperature 350 °F	Recommended Cure Cycle
	240 min @Temperature 227 °C	4.00 hour @Temperature 440 °F	Postcure Cycle, after 30 minute ramp up cycle
Shelf Life	3.00 Month @Temperature 4.44 °C	3.00 Month @Temperature 40.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Natural
Total Product Weight (oz/yd2)	52	Arlon SQA-TMS-025